The Strain-Hardening Behavior of Partially Austenitized and the Austempered Ductile Irons with Dual Matrix Structures

@article{Kll2008TheSB,
  title={The Strain-Hardening Behavior of Partially Austenitized and the Austempered Ductile Irons with Dual Matrix Structures},
  author={Volkan Kılıçlı and M. Erdoğan},
  journal={Journal of Materials Engineering and Performance},
  year={2008},
  volume={17},
  pages={240-249}
}
In the current study, an unalloyed ductile iron containing 3.50 C wt.%, 2.63 Si wt.%, 0.318 Mn wt.%, and 0.047 Mg wt.% was intercritically austenitized (partially austenitized) in two-phase regions (α + γ) at different temperatures for 20 min and then was quenched into salt bath held at austempering temperature of 365 °C for various times to obtain different ausferrite plus proeutectoid ferrite volume fractions. Fine and coarse dual matrix structures (DMS) were obtained from two different… Expand
21 Citations
Intercritically Austenitized Quenched and Tempered Ductile Iron
  • 13
Microstructure and Mechanical Properties of ADI Depending on Austenitization Methods and Parameters
  • 6
  • Highly Influenced
  • PDF
Predicting ADI mechanical properties
  • 3
  • PDF
Intercritical Heat Treatments In Ductile Iron And Steel
  • 3
  • Highly Influenced
  • PDF
Influence of gradual austenitizing on chosen properties of ADI
  • 2
  • PDF
...
1
2
3
...

References

SHOWING 1-10 OF 28 REFERENCES
Strain-induced martensite in ADI alloys
  • 60
...
1
2
3
...