Effect of microstructure and mechanical properties on the erosion of 18 Ni ( 250 ) maraging steel and aluminum alloys

Abstract

Specimens of 18 Ni (250) maraging steel were solution treated and aged at the temperatures of 480® C, 590® C, and 650® C for varying times up to a maximum of 24 hours. Solution annealed specimens were also cold rolled to varying amounts. The erosion behavior of these specimens was studied in a sand-blast type test rig. The tests were conducted under ambient… (More)