Effect of fluxes on cracking during ESS of steel with 70

@inproceedings{Zhang1994EffectOF,
  title={Effect of fluxes on cracking during ESS of steel with 70},
  author={Jingying Zhang},
  year={1994}
}
Effect of F l u Composition on Cracking during ESS of Steel with 70130 Cupronickel Strip Jingying Zhang, M. S. Oregon Graduate Institute of Science & Technology, 1994 Supervising Professor: Jack H. Devletian The effect of flux composition on the weldability of multi-layer cladding deposited on steel with 70130 cupronickel strip electrodes by the electrosIag surfacing (ESS) process was investigated. For comparison purpose, two nearly similar commercial fluxes were used: Flux 1 caused severe… Expand

References

SHOWING 1-8 OF 8 REFERENCES
Microsegregation in Partially Melted Regions of 70Cu-30Ni Weldments Evidence supports an hypothesis that explains the mechanism of partial melting and its effects
The partially melted regions of gas tungsten-arc welds made in a 70Cu-30Ni alloy were studied. An hypothesis explaining the mechanism of partial melting was ad­ vanced and tested by employingExpand
AVAILABILITY AND TYPICAL USES OF COPPER ALLOY PLATE AND SHEET
COPPER ALLOYS IN MARINE ENVIRONMENTS TODAY AND TOMORROW
Effect of Alloying Additions on the Weldability of 700-30NiW, Weld
  • J.,
  • 1978
Weldability of a Chromium Strengthened Copper-Nickel Alloy", Weld
  • J.,
  • 1969
Varestraint meldability) Testing of Cast 70Cu-30Ni AlIoy " Weld
  • J., Aug.
  • 1968
Some Factors Affecting the Weldability of the Cupro-Nickels", Weld
  • J.,
  • 1960