Broadband near-IR emission from cubic perovskite KZnF(3):Ni(2+) nanocrystals embedded glass-ceramics.


Transparent KF-ZnF(2)-SiO(2) glass-ceramics were prepared with the precipitation of KZnF(3)Ni(2+) nanocrystals. During excitation with a wavelength of 405 nm at room temperature, a broadband near-IR emission centered at 1695 nm with the FWHM of more than 350 nm was observed, which is originated from the T(2g)3(F3)→A(2g)3(F3) transition of octahedral Ni(2… (More)
DOI: 10.1364/OL.40.005263