A cracking oxygen story: a new view of stress corrosion cracking in titanium alloys

@article{Josepha2020ACO,
  title={A cracking oxygen story: a new view of stress corrosion cracking in titanium alloys},
  author={Sudha Josepha and Paraskevas Kontis and Yanhong Chang and Yitong Shi and Dierk Raabe and Baptiste Gault and David Dye},
  journal={arXiv: Materials Science},
  year={2020}
}
Titanium alloys can suffer from halide-associated stress corrosion cracking at elevated temperatures e.g. in jet engines, where chlorides and Ti-oxide promote the cracking of water vapour in the gas stream, depositing embrittling species at the crack tip. Here we report, using isotopically-labelled experiments, that crack tips in an industrial Ti-6Al-2Sn-4Zr-6Mo alloy are strongly enriched (>5 at.%) in oxygen from the water vapour, far greater than the amounts (0.25 at.%) required to embrittle… Expand

Figures from this paper

References

SHOWING 1-10 OF 40 REFERENCES
The mechanisms of hot salt stress corrosion cracking in titanium alloy Ti-6Al-2Sn-4Zr-6Mo
Abstract Hot salt stress corrosion cracking in Ti 6246 alloy has been investigated to elucidate the chemical mechanisms that occur. Cracking was found to initiate beneath salt particles in theExpand
Hydrogen in Ti and Zr alloys: industrial perspective, failure modes and mechanistic understanding
  • T. Chapman, D. Dye, D. Rugg
  • Materials Science, Medicine
  • Philosophical Transactions of the Royal Society A: Mathematical, Physical and Engineering Sciences
  • 2017
TLDR
An overview of the role hydrogen has to play through the material life cycle is provided, including the relationship between alloy design and manufacturing process windows, the role of hydrogen in degradation and failure mechanisms and some of the underpinning metallurgy. Expand
Brittle behavior of ductile metals during stress-corrosion cracking
Abstract The transgranular stress-corrosion cracking of ductile alloys (and at least one pure metal) leads to a fracture appearance characteristic of cleavage. The experimental and theoreticalExpand
Hydrogen embrittlement of α titanium: In situ tem studies
The effect of hydrogen on fracture in the h.c.p. α Ti-4 wt % Al alloy and the role of titanium hydride in the fracture process have been studied by deforming samples in situ in a high-voltageExpand
Hydrogen-Assisted Degradation of Titanium Based Alloys
Titanium base alloys are among the most important advanced materials for a wide variety of aerospace, marine, industrial and commercial applications, due to their high strength/weight ratio and goodExpand
The Role of Oxidized Carbides on Thermal-Mechanical Performance of Polycrystalline Superalloys
Oxidized MC carbides which act as main crack initiation sites in a polycrystalline superalloy under thermal-mechanical fatigue (TMF) conditions at 850 °C were studied. Microstructural observations inExpand
Origin of dramatic oxygen solute strengthening effect in titanium
TLDR
It is reported that the intense hardening effect of dilute oxygen solutes in pure α-Ti is due to the interaction between oxygen and the core of screw dislocations that mainly glide on prismatic planes, establishing a highly effective mechanism for strengthening by interstitial solutes. Expand
The effects of hydrogen on the deformation and fracture of β-titanium
Abstract The hydrogen-induced ductile–brittle transition in the BCC β -titanium alloy, Timetal® 21S, occurs abruptly at a critical hydrogen concentration that decreased with decreasing tensile testExpand
The influence of oxygen on the structure, fracture, and fatigue crack propagation behavior of Ti-8.6 Wt Pct Al
The effect of interstitial oxygen content on the structure, fracture, and fatigue crack propagation (FCP) behavior of Ti-8.6 wt pct Al was studied. Increasing oxygen was seen to raise the tensileExpand
The Dislocation Mechanism of Stress Corrosion Embrittlement in Ti-6Al-2Sn-4Zr-6Mo
An observation of the dislocation mechanisms operating below a naturally initiated hot-salt stress corrosion crack is presented, suggesting how hydrogen may contribute to embrittlement. TheExpand
...
1
2
3
4
...