Zn4O(1,4-benzenedicarboxylate)3 (MOF-5) Steven S. Kaye,† Anne Dailly,‡,§ Omar M. Yaghi,¶ and Jeffrey R. Long*,† Department of Chemistry, UniVersity of California, Berkeley, California 94720, Chemical and EnVironmental Sciences Laboratory, General Motors Corporation, Warren, Michigan 48090, College of Engineering, Purdue UniVersity, West Lafayette, Indiana(More)
The porosity and hydrogen storage properties for the dehydrated Prussian blue analogues M3[Co(CN)6]2 (M = Mn, Fe, Co, Ni, Cu, Zn) are reported. Argon sorption isotherms measured at 87 K afford BET surface areas ranging from 560 m2/g for Ni3[Co(CN)6]2 to 870 m2/g for Mn3[Co(CN)6]2; the latter value is comparable to the highest surface area reported for any(More)
The adsorption of molecular hydrogen in the Prussian blue analogue Cu3[Co(CN)6]2 was investigated using high-resolution neutron powder diffraction and neutron vibrational spectroscopy. Rietveld structural refinement of the neutron data for hydrogen loadings of 1, 2, and ∼2.3 H2/Cu showed that the hydrogen was absorbed at two sites within the structure. The(More)
Despite the large number of metal-organic frameworks that have been studied in the context of post-combustion carbon capture, adsorption equilibria of gas mixtures including CO2, N2, and H2O, which are the three biggest components of the flue gas emanating from a coal- or natural gas-fired power plant, have never been reported. Here, we disclose the design(More)
The impact of coordinatively-unsaturated alkali-metal ions on hydrogen adsorption is studied in dehydrated variants of the compounds A(2)Zn(3)[Fe(CN)(6)](2).xH(2)O (A = H, Li, Na, K, Rb), revealing maximum adsorption enthalpies that vary from 7.7 kJ mol(-1) for A = Na to 9.0 kJ mol(-1) for A = K.
A new series of novel mast cell tryptase inhibitors is reported, which features the use of an indole structure as the hydrophobic substituent on a m-benzylaminepiperidine template. The best members of this series display good in vitro activity and excellent selectivity against other serine proteases.
Dehydration of the Prussian blue analogues CsNi[Cr(CN)(6)] x 2 H(2)O (1) and Cr(3)[Cr(CN)(6)](2) x 10 H(2)O (2) affords two new microporous magnets: CsNi[Cr(CN)(6)] (1d) and Cr(3)[Cr(CN)(6)](2) x 6 H(2)O (2d). Compounds 1d and 2d maintain the Prussian blue structure, and N(2) adsorption measurements at 77 K show them to be microporous with BET surface areas(More)
The porosity and hydrogen storage properties of the dehydrated Prussian blue type solids Ga[Co(CN)6], Fe4[Fe(CN)6]3, M2[Fe(CN)6] (M = Mn, Co, Ni, Cu), and Co3[Co(CN)5]2 are reported and compared to those of M3[Co(CN)6]2 (M = Mn, Fe, Co, Ni, Cu, Zn). Nitrogen sorption measurements suggest partial framework collapse for M2[Fe(CN)6] (M = Co, Ni) and(More)
The lack of a high capacity hydrogen storage material is a major barrier to the implementation of the hydrogen economy. To accelerate discovery of such materials, we have developed a high-throughput workflow for screening of hydrogen storage materials in which candidate materials are synthesized and characterized via highly parallel ball mills and(More)