A novel method for analysis of benzylic ether type lignin–carbohydrate bonds has been developed by using model compounds. Four diastereomers of model compound 3-(4-hydroxy-3-methoxyphenyl)-2-(2-methoxyphenoxy)-3-(methyl β-d-glucopyranoside-6-O-yl)-1-propanol (GGMGP), were ozonized in acetic acid/water/methanol 16 : 3 : 1 for 1 h at 0°C. The product from(More)
Methylβ-d-xylopyranoside was allowed to react withβ-O-4-type quinone methide without a catalyst to elucidate the reactivities of secondary hydroxyl groups at the C2, C3, and C4 positions. Benzyl ether-type lignin-carbohydrate complex (LCC) compounds linked at the C2 and C4 positions were predominant, at a ratio of 2∶3. However, the reactivity of the(More)
Evidence for the presence of lignin-carbohydrate bonds of the benzylic ether type in wood and pulps may be obtained by use of ozonation treatment to selectively degrade the lignin. It was found that the benzyl ether bond in 3-(4-hydroxy-3-methoxyphenyl)-2-(2-methoxy-phenoxy)-3-(methyl-β-d-glucopyranosid-6-O-yl)-1-propanol was rather stable during ozonation(More)
To develop a new nonchlorine bleaching technology, hardwood and softwood kraft pulps, before and after oxygen-alkali predelignification, were treated with dilute sulfuric acid solutions (pH 1.0-1.8) at 100°C for 1 h and then extracted with aqueous sodium hydroxide at 70°C for l h. Hardwood kraft pulp was successfully bleached. The delignification(More)
To investigate the bleaching mechanism, a lignincarbohydrate complex (LCC) model compound, a vinyl ether-type lignin model dimer, and a hexeneuronic acid model compound were treated with dilute sulfuric acid of different pHs. Beech kraft pulp and red pine kraft pulp were also treated with dilute sulfuric acid and then extracted with aqueous alkali. The(More)
The purpose of this study was to investigate the behavior of lignin and carbohydrates in kraft pulps during sulfuric acid bleaching. Beech kraft pulp and red pine kraft pulp were bleached with dilute sulfuric acid at pH 1.3 with addition of sodium nitrate and sodium nitrite at 100°C for 1 h. The pulps were then extracted with aqueous sodium hydroxide(More)
Acetylated fibers with a 24.8% weight gain by acetylation were ozonated with 0%–2.0% ozone on fibers. Fiberboards were then made from these treated fibers. The internal bond and bending strength of the acetylated fiberboards increased drastically with increasing ozone charge up to 0.5%–1.0%, whereas the thickness swelling of the fiberboards decreased. Ozone(More)