Electronic structure of d orbital states in transition metals is a key factor for their physical properties and chemical functions. Copper and intermetallic compound PdZn have good catalysis function for the methanol steam reforming reaction. Tsai et al. showed that from results of XPS measurements the d electronic structure of PdZn was similar with that of(More)
Three different porous Au catalysts that exhibit high catalytic activity for CO oxidation were prepared by the leaching of Al from an intermetallic compound, Al2Au, with 10 wt. %-NaOH, HNO3, or HCl aqueous solutions. The catalysts were investigated using Brunauer-Emmett-Teller measurements, synchrotron X-ray powder diffraction, hard X-ray photoelectron(More)
A fine layered nanocomposite with a total thickness of about 200 nm was formed on the surface of an Al63Cu25Fe12 quasicrystal (QC). The nanocomposite was found to exhibit high catalytic performance for steam reforming of methanol. The nanocomposite was formed by a self-assembly process, by leaching the Al-Cu-Fe QC using a 5 wt% Na2CO3 aqueous solution(More)
We investigated the catalytic properties of a CuNi solid solution and Pd for methanol-related reactions and associated valence electronic structures. Calculations and X-ray photoelectron spectroscopy measurements revealed that the CuNi alloy has a similar valence electronic structure to Pd and hence they exhibited similar CO selectivities in steam reforming(More)
Nanoporous gold (NPG) prepared by de-alloying Al2Au exhibits correlation between the high catalytic reactivity towards CO oxidation and the density of twinning defects in the fcc lattice of NPG. It was also discovered that on the internal surface of NPG, quite common twinning defects can create close-packed rows of six-coordinated catalytically active Au(More)
We describe a new mechanism for creation of catalytically active sites in porous gold. Samples of porous gold prepared by de-alloying Al2Au exhibit a clear correlation between the catalytic reactivity towards CO oxidation and structural defects in the fcc lattice of Au. We have found that on the stepped {211} surfaces quite common twin boundary defects in(More)