AIM To compare regional bond strength in different thirds of the root canal, among glass fiber-reinforced (FRC) endodontic posts luted with different cements, using the push-out test. MATERIAL AND METHODS Sixty extracted human anterior teeth were endodontically treated with gutta-percha and AH Plus sealer. The crown portion was removed, and a dowel space(More)
The objective of this study was to measure the demineralization capacity of 10% and 20% citric acid and 17% EDTA after three time periods and to determine whether it was modified by the addition of 1% of commercial chlorhexidine (CHX). Three slices of 2-mm thickness were cut from the cervical third of the root of ten bovine incisors and sectioned into two(More)
Cuspal deflection produced by polymerization shrinkage was measured after using different composite restoration techniques. This study included 30 healthy premolars embedded in acrylic resin connected to a system that simulated intrapulpal pressure. A small ball was attached to each cuspal vertex as a reference point for intercuspal distance measurements. A(More)
OBJECTIVES To investigate the bond strength and seal ability produced by AH Plus/gutta-percha, EndoREZ and RealSeal systems to root canal dentin. MATERIAL AND METHODS Sixty extracted single-root human teeth, instrumented manually to size 40, were divided into three groups (n=20) according to the sealer used; G1: AH Plus, G2: EndoREZ, and G3: RealSeal(More)
STATEMENT OF PROBLEM Some clinical situations may require the repair of a secondary polymerized or aged composite. The higher indirect resin conversion rate may prove to be a disadvantage if a repair procedure based on covalent bonding from unreacted methacrylate groups is attempted. PURPOSE This study evaluated the effectiveness of different combinations(More)
PURPOSE To measure in vitro the cuspal deflection produced by polymerization shrinkage and occlusal loading in mesio-occlusal (MO) and mesio-occlusal-distal (MOD) bonded composite restorations. MATERIALS AND METHODS Twenty first premolars were studied, attaching a small crystal ball to each cusp vertex as a reference point for intercuspal distance(More)
STATEMENT OF PROBLEM Coronal leakage can produce contamination of periapical tissues, resulting in endodontic failure. PURPOSE The purpose of this in vitro study was to evaluate the ability of 2 sealers to prevent coronal leakage in canals filled with gutta-percha and prepared for cast dowels but without coronal sealing. MATERIAL AND METHODS The crowns(More)
OBJECTIVES The objective of this study was to determine microtensile bond strength (μTBS) to dentin of three self-adhesive and a total-etch resin cements used for luting different treated indirect composites. MATERIALS AND METHODS Composite overlays (Filtek Z250) were prepared. Their intaglio surfaces were ground with 600-grit SiC papers and randomly(More)
OBJECTIVES To determine the influence of different etching times (5, 15 or 30 s) on the morphology and micro-tensile bond strength (muTBS) of primary dentin. METHODS For muTBS study, nine primary molars were randomly distributed in three experimental groups. Three Class I cavities per tooth were drilled and etched (37% orthophosphoric acid gel for 5, 15(More)
The aim of the study was to determine the interfacial morphology and bond strength of three current self-etching adhesives (SEAs) to primary dentin and to evaluate the effect of introducing an additional step of phosphoric acid etching. Three human primary molars were assigned to each adhesive group for testing microtensile bond strength (microTBS) and(More)