To provide gist of DC AA 5052 and CC AA 5052 aluminum alloy to industry production and application, the texture variation of cold rolled sheets through thickness direction was studied by X-ray diffraction method, and the difference in texture at surface, quarter and center layer was analyzed. The hot plates of direct chill cast (DC) AA 5052 and continuous(More)
For improvement the processing and gaining uniformity texture structure and performance the thickness direction of direct chill cast DCAA 5052 aluminum alloy band after first hot rolling with different reduction, the material was annealed at 454 degrees C and then cold rolling with different reduction, we test and examined the texture at surface, quarter(More)
For improvement of the processing and gaining uniformity texture structure and performance of direct chill cast CCAA 5052 aluminum alloy band after first hot rolling with different reduction, the material was annealed at 454 degrees C and then cold rolling with different reduction was conducted, the texture at surface, quarter and center layer of the sample(More)
At present the study of relation between microstructure, texture and performance of CC 5083 aluminium alloy after cold tolling and recrystallization processes is still finitude. So that the use of the CC 5083 aluminium alloy be influenced. Be cased into electrical furnace, hot up with unlimited speed followed the furnace hot up to different temperature and(More)