Ti-aluminides-reinforced Ti-matrix composites were fabricated from 0.04mm-thick Ti foils and 0.012mmand 0.024mm-thick aluminum foils, in a process using a pulsed-current hot pressing (PCHP) equipment, and the effect of reaction temperature on properties of the composites was investigated. The composites were of laminated structure and composed of Ti and(More)
The correlation between the magnetic properties and micro-structure of electroless-plated CoNiP perpendicular magnetic recording media was investigated. By adjusting the plating bath factors, the perpendicular coercivity, H<inf>c¿</inf>, of the film can be controlled to up to 1500 Oe without changing the saturation magnetization M<inf>s</inf> and the shapes(More)
The magnetic properties and microstructure of electroless-plated CoNiReP films, which varied primarily in their cobalt content, were investigated in order to clarify the origin of their magnetic anisotropy. The films which showed perpendicular magnetic anisotropy contained approx. 25 to 40% cobalt. They also had a higher crystallinity and better c-axis(More)
  • 1