S and N co-doped, few-layered graphene oxide is synthesized by using pyrimidine and thiophene as precursors for the application of the oxygen reduction reaction (ORR). The dual-doped catalyst with pyrrolic/graphitic N-dominant structures exhibits competitive catalytic activity (10.0 mA cm(-2) kinetic-limiting current density at -0.25 V) that is superior to(More)
This work addresses the chemical nature of the catalytic activity of X-ray "pure" CoO nanocrystals. All samples were prepared by a solvothermal reaction route. X-ray diffraction indicates the formation of CoO in a cubic rock-salt structure, while infrared spectra and magnetic measurements demonstrate the coexistence of CoO and Co 3O 4. Therefore, X-ray(More)
High-purity anatase TiO(2) nanoparticles were prepared using a low-temperature sol-gel route. The as-prepared sample was characterized by X-ray diffraction, transmission electron microscopy, infrared spectroscopy, thermogravimetric analysis, UV-vis spectroscopy, and photoluminescence. It is shown that the as-prepared sample crystallized in a pure anatase(More)
Development of inexpensive and sustainable cathode catalysts that can efficiently catalyze the oxygen reduction reaction (ORR) is of significance in practical application of fuel cells. Herein we report the synthesis of sulfur and nitrogen dual-doped, ordered mesoporous carbon (SN-OMCs), which shows outstanding ORR electrocatalytic properties. The material(More)
Recently, many studies have shown the potential use of circulating exosomes as novel biomarkers for monitoring and predicting a number of complex diseases, including cancer. However, reliable and cost-effective detection of exosomes in routine clinical settings, still remain a difficult task, mainly due to the lack of adequately easy and fast assay(More)
Platinum is commonly chosen as an electrocatalyst used for oxygen reduction reaction (ORR). In this study, we report an active catalyst composed of MnO2 nanofilms grown directly on nitrogen-doped hollow graphene spheres, which exhibits high activity toward ORR with positive onset potential (0.94 V vs RHE), large current density (5.2 mA cm-2), and perfect(More)
This work initiated a systematic study on the chemical nature of organic coating for monodispersed nanoparticles and its impact on the defect chemistry and the relevant properties. Monodispersed TiO(2) nanoparticles were prepared by a nonhydrolytic sol-gel reaction, which showed features of uniform diameter distribution around 5.2 nm, high crystallinity,(More)