Internal-external transition for the oxidation of Fe-Cr-Ni austenitic stainless steels in steam
Several Fe-Cr-Ni austenitic stainless steels (Cr wt.%: 13–25, Ni wt.%: 15) were oxidized in steam for 1000 hr at 500–900°C. The oxide scales were examined and categorized with respect to the chromiumExpand
  • 85
  • 1
Corrosion behaviour of austenitic stainless steels in the high chloride-containing environment
Abstract The corrosion behaviour of austenitic stainless steels was studied by repeated cycles of immersion in saturated chloride solution and heating. In addition, corrosion behaviour was observedExpand
  • 28
  • 1
Particle erosion behaviour of boiler tube materials at elevated temperature
Abstract The particle erosion behaviour of typical boiler tube materials, including carbon steel, low alloy steels and austenitic steels, at elevated temperatures up to 650 °C was studied usingExpand
  • 32
  • 1
Scaling of Austenitic Stainless Steels and Nickel-Base Alloys in High-Temperature Steam at 973 K
Abstract Scaling of commercial high-strength austenitic stainless steels and nickel-base alloys, possible candidates for ultra-supercritical (USC) boiler-tube materials, was studied in atmospheric ...
  • 43
The Effects of Small Additions of Yttrium on the High-Temperature Oxidation Resistance of a Si-Containing Austenitic Stainless Steel
The oxidation characteristics of a 19Cr–10Ni–1.5Si alloy with and without 0.03Y have been examined using scanning-electron microscopy, secondary-ion mass spectroscopy and transmission-electronExpand
  • 28
Recent Advances in Coated Steels Used for Automobile
Looking at developments in the production of new steel sheets in the Japanese steel and car industries, this volume includes the following topics: corrosion resistance and workability of precoatedExpand
  • 11
Effect of Small Amounts of Ni on Liquid-Cu Embrittlement in Hot-Rolled Mild Steel After High-Temperature Oxidation
The effects of additions of as little as 0.02%Nito mild steel on the morphology of the scale-steelinterface and surface cracking were studied duringhigh-temperature oxidation and subsequentExpand
  • 16
High Temperature Oxidation Behaviour of High Al Content Ferritic and Austenitic Stainless Steels With and Without Rare-Earth Element Addition
The oxidation behaviour of austenitic and ferritic alloys containing 4% Al and rare-earth element addition of (La + Ce) has been investigated, and comparisons made to an austenitic alloy with no suchExpand
  • 10
Fabrication and properties of corrosion resistant TP347H stainless steel
A grain refining process has been developed for TP347H tubes, where grain size as fine as GS No. 8 can be obtained even at higher solution treating temperatures. Grain refinement is caused by theExpand