A high-temperature solid-state method was used to synthesize the Ho3+- and Yb3+-codoped cubic Lu2O3 powders. The crystal structures of the as-prepared powders were characterized by X-ray diffraction. The energy-transfer (ET) phenomenon between Ho3+ ions and Yb3+ ions was verified by the steady-state spectra including visible and near-infrared (NIR) regions.(More)
Relaxed InyGa1_yAs epilayers grown on (0 0 1) GaAs are known to exhibit a cross-hatched surface with ridges running along the [1 1 0] and 1⁄21 % MnxAs epilayers grown on such buffer layers can 1 0] directions. We find that Ga1_x have as-grown Curie temperatures (TC) that are higher than the as-grown 110 K value typical of Ga1_xMnxAs/GaAs heterostructures.(More)
The monochromaticity improvement of green upconversion (UC) in Lu2O3:Yb3+/Ho3+ powders has been successfully realized by tridoping Eu3+. The integral area ratio of green emission to red emission of Ho3+ increases 4.3 times with increasing Eu3+ doping concentration from 0 to 20 mol %. The energy transfer (ET) mechanism in the Yb3+/Ho3+/Eu3+ tridoping system(More)
Nanosized Yb(3+) and Er(3+) co-doped β-NaYF4 cores coated with multiple β-NaYF4 shell layers were synthesized by a solvothermal process. X-ray diffraction and scanning electron microscopy were used to characterize the crystal structure and morphology of the materials. The visible and near-infrared spectra as well as the decay curves were also measured. A(More)
The Pr(3+) and Yb(3+) codoped β-NaLuF4 hexagonal nanoplates with a size of 250 nm × 110 nm were synthesized by a solvothermal process. X-Ray diffraction and scanning electron microscopy were used to characterize the crystal structure and morphology of the materials. The visible and near infrared spectra as well as the decay curves of Pr(3+):(3)P0 level were(More)
The red upconversion (UC) emission of Eu3+ ions in Lu2O3: Yb3+/Eu3+ powders was successfully enhanced by tridoping Ho3+ ions in the matrix, which is due to the bridging function of Ho3+ ions. The experiment data manifest that, in Yb3+/Eu3+/Ho3+ tridoped system, the Ho3+ ions are first populated to the green emitting level 5F4/5S2 through the energy transfer(More)
The Yb(3+) and Er(3+) codoped orthorhombic LuF3 rectangular nanocrystals (NCs) with the size of about 10nm were synthesized by a facile and effective solvothermal process. X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), upconversion (UC) luminescence spectra and decay curves were(More)