Zu Beginn der Arbeit wird über den Kenntnisstand bei der Herstellung von mitteldichten Faserplatten (MDF) berichtet. Im Anschluß daran werden Ergebnisse von Untersuchungen zum Aufschluß von Buchen- und Kiefernholz nach dem TMP- und CTMP-Verfahren unter verschiedenen Bedingungen aufgezeigt. An den hergestellten Fasern wurden verschiedene(More)
Chips from pine wood were subjected to thermo-mechanical pulping (TMP) at 140 and 180 oC for 5 minutes, whereas the cooked chips were defibrated using a single disk pressurized refiner at the same temperatures (140 and 180 oC). The fibres were tested for some of their morphological properties including fibre length, fibre width, cellwall thickness.(More)
IR-spectra of TMP and CTMP prepared from pine wood and UF-bonded MDF made from pine wood show characteristic differences. The typical band for carbonyl groups (C=O-groups) at wave number about 1740 cm-1 is strong in pine wood, but appears relatively weak in TMP and especially in CTMP made thereof. In UF-bonded MDF made from pine wood the band at about 1740(More)
Thermo-mechanical (TMP) and chemo-thermo-mechanical pulps (CTMP) were prepared from pine wood and from UF-bonded MDF made from pine wood. For preparing TMP pine chips as well as UF-bonded MDF were digested under pressure at 170 °C. Thereafter, the digested chips and MDF were defibrated at 170 °C using a single disc refiner. CTMP was prepared from pine wood(More)
Die Untersuchungen betreffen die Eignung von TMP (thermo-mechanisch hergestellte Fasern) aus gebrauchten Holzspan- und -faserplatten als Rohstoff für die Herstellung von mitteldichten Faserplatten. Die Untersuchungsergebnisse lassen folgende Schlüsse zu: TMP aus gebrauchten Holzspan- und Holzfaserplatten weisen charakteristische morphologische und chemische(More)
TMP (thermo-mechanical pulps) and CTMP (chemo-thermo-mechanical pulps) were made from pine wood and recycling MDF, which has been prepared from pine wood too. The fibres were tested for their wettability using the method developed by Roffael et al (2002). The results reveal that TMP are much less wettable in comparison to CTMP from the same wood. Moreover,(More)
Thermo-mechanical (TMP) and chemo-thermo-mechanical pulping (CTMP) of UF-bonded MDF induce considerable degradation of the UF-resin in the board and lead to a conspicuous increase in the content of water extractives of the fibres. Moreover, the water extractives of the fibres have a higher pH-value and a lower buffering capacity as well as higher acetate(More)
Mitteldichte Faserplatten (MDF) wurden aus thermo-mechanischem Holzstoff (TMP) und chemo-thermo-mechanischem Holzstoff (CTMP) der Kiefer hergestellt. Als Bindemittel wurden ein mit Melamin verstärktes Harnstoff-Formaldehydharz (UF-Harz) und ein Klebstoff auf Basis von polymerem Diisocyanat (PMDI) eingesetzt. An den hergestellten MDF wurden neben den(More)
Es wurden zwei Methoden auf ihre Eignung zur Erfassung der Hydrophobierung von thermomechanischen Faserstoffen (TMP) durch Paraffine untersucht, namentlich die Methode zur Erfassung der Benetzung von Holzfasern (Benetzbarkeit) (Roffael et al. 2002) sowie der Cobb-Test (EN 20535, ISO 535), der in der Papierindustrie für die Bestimmung des(More)