Learn More
The effects of nano-SiO(2) on three ash particle sizes in mortar were studied by replacing a portion of the cement with incinerated sewage sludge ash. Results indicate that the amount of water needed at standard consistency increased as more nano-SiO(2) was added. Moreover, a reduction in setting time became noticeable for smaller ash particle sizes. The(More)
Sewage sludge incineration is applied extensively in highly populated cities as a final sludge treatment. In this study, incinerated ash was utilized as an additive to clay to manufacture glaze tiles. Four different amounts of ash (0, 15, 30, and 45%) were added, and five glaze concentrations (0.03, 0.06, 0.1, 0.15, and 0.2 g/cm2) were applied on the(More)
In this article, glaze with different colorants was applied to tile specimens manufactured by incinerated sewage sludge ash (ISSA) and clay. Improvements using different amounts of colorants, and glaze components and concentrations on tile bodies were investigated. Four different proportions of clay (by weight ratio) were replaced by ISSA. Tiles of size 12(More)
This study investigated the effects of phosphate on the hydration characteristics of three eco-cement clinkers made utilizing water purification sludge ash, sewage sludge ash and industry sludge ash. Analytical results demonstrate that the eco-cement A (ECO-A) pastes had a similar setting times, final setting times, compressive strengths and degree of(More)
Sewage sludge ash has been widely applied to cementitious materials. In this study, in order to determine effects of nano-SiO(2) additives on properties of sludge/fly ash mortar, different amounts of nano-SiO(2) were added to sludge/fly ash mortar specimens to investigate their physical properties and micro-structures. A water-binding ratio of 0.7 was(More)
In this study, the strength of soft cohesive subgrade soil was improved by applying sewage sludge ash as a soil stabilizer. Test results obtained were compared with earlier tests conducted on soil samples treated with fly ash. Five different proportions of sludge ash and fly ash were mixed with soft cohesive soil, and tests such as pH value, compaction,(More)
This study investigated and analyzed the effects of the heating temperature on the properties of the sintered sewage sludge ash. The results indicated that the water absorption rate of the sintered sewage sludge ash samples decreased when the firing temperature was increased from 800 to 900 degrees C. When the heating temperature reached 1000 degrees C, the(More)
In order to extend the recycling of waterworks sludge to engineering applications, this paper addresses the influence of nano-SiO2 on incinerated waterworks sludge ash (IWSA) cement paste attacked by sulfate. Tests were performed such as length measurement for volume change, compressive strength, weight loss, and micro-structural testing using scanning(More)
To improve the drawbacks caused by the sludge ash replacement in mortar, the previous studies have shown that the early strength and durability of sludge ash/cement mortar are improved by adding nano-silicon dioxide (nano-SiO2) to mortar. In this article, three types of nano-SiO2--SS, HS, and SP (manufacturer code names)--were applied to sludge ash/cement(More)
In this study, incinerated sewage sludge ash (ISSA) is mixed with cement in a fixed ratio of 4:1 for use as a stabilizer to improve the strength of soft, cohesive, subgrade soil. Five different ratios (in wt%: 0%, 2%, 4%, 8%, and 16%) of ISSA/cement admixture are mixed with cohesive soil to make soil samples. In order to understand the influences of(More)